    Synthesis and Characterization of Eggshell-derived Hydroxyapatite for Dental Implant Applications
    (EDP Sciences, 2023-01-01) Jamiu Kolawole Odusote; Adekunle Akanni Adeleke; Peter Pelumi Ikubanni; Peter Omoniyi; Tien-Chien Jen; G. Odedele; Jude A. Okolie; Esther Titilayo Akinlabi
    Hydroxyapatite (HAp) production from eggshells for dental implant purposes involved a novel approach utilizing a wet chemical precipitation technique. The eggshells, finely ground to a size below 250 μm, underwent calcination at a high temperature of 900°C for 2 hours. This thermal treatment facilitated the conversion of calcium carbonate into calcium oxide (CaO) while eliminating any organic components in the eggshell. To initiate the synthesis of HAp, a solution comprising 0.6 M phosphoric acid was added to the CaO dispersed in water. The resulting mixture was allowed to undergo aging at different time intervals ranging from 0 to 24 hours, promoting the formation of HAp. Subsequently, the HAp particles were oven-dried at 100°C for 2 hours to remove residual moisture. Finally, the dried particles were sintered at 1200°C in a muffle furnace to achieve the desired properties for dental implant applications. XRD peaks at 25, 33, 40, and 50° confirm the synthesized material as HAp. Vibrational modes of phosphate (PO43-), hydroxyl (OH-), and carbonate (CO32-) groups indicate carbonated HAp. Synthesized HAp holds potential for biomedical applications.